86 μm 200 mm×20 m Roll Aluminum-Plastic Film
POUCH CELL ALUMINUM-PLASTIC FILM
|
|||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
Purchase ConfirmationConfiguration: Confirm thickness, width, and length before ordering. Quotation Check: Confirm the title dimensions and pack format before production or ordering release.
|
Brand: ATOMFAIR®
This aluminum-plastic film requires heat sealing at 180–190°C with 0.2 MPa pressure for 2 seconds to achieve a minimum heat seal strength of 29.4 N/15 mm. The laminate must maintain a molding depth of at least 5.0 mm and a solvent retention below 5 mg/m² to ensure pouch integrity.
- Hot Sealing Condition: Hot sealing must be performed at 180–190°C to achieve proper bond formation.
- Heat Seal Strength: Heat seal strength must exceed 29.4 N/15 mm when sealed at 200°C, 0.2 MPa for 2 seconds.
- Molding Depth: The film must support a molding depth of at least 5.0 mm without failure.
- Solvent Retention: Solvent retention must be less than 5 mg/m² to avoid contamination.
- Laminate Strength: Laminate strength must exceed 2 N/15 mm for Nylon/Al and 5 N/15 mm for Al/CPP interfaces.
What is the minimum molding depth achievable with the 86 μm aluminum-plastic film, and what heat seal strength can be expected?
The film achieves a molding depth of at least 5.0 mm. Under optimal hot sealing conditions at 180-190°C, 0.2 MPa, and 2 seconds, the heat seal strength exceeds 29.4 N/15 mm width. This combination supports reliable pouch cell sealing.
What are the precise hot sealing parameters required for this aluminum-plastic film to ensure proper adhesion?
The recommended hot sealing condition is 180-190°C at 0.2 MPa for 2 seconds on heatsealing equipment. The film's heat seal strength is guaranteed to be greater than 29.4 N/15 mm under these conditions, ensuring a robust seal.
What are the critical quality metrics for surface defects and solvent retention in this pouch film?
The film has a mat finish surface quality. Impurities must be ≤1 mm in diameter, fish eyes ≤2 mm (clear) or ≤1 mm (coloured). Solvent retention is less than 5 mg/m², ensuring low contamination risk. The slip factor (CPP/CPP) is less than 1.0, which may affect handling during stacking.
This 86 μm aluminum-plastic film roll offers high laminate and heat seal strength, along with good moisture barrier and electrical insulation, making it suitable for pouch cell assembly. However, the hot sealing process requires precise temperature control (180-190°C) and specific pressure/time parameters, which may necessitate dedicated heat sealing equipment.
Positive
- Robust laminate and seal strength: Laminate strength exceeds 2 N/15 mm for Nylon/Al and 5 N/15 mm for Al/CPP, with heat seal strength >29.4 N/15 mm at 200°C, 0.2 MPa, 2 sec, ensuring reliable pouch sealing.
- Excellent barrier and insulation: Moisture vapor/O2 transmission rate is specified at 200 ppm per 5 years, and electrical insulation is rated as good, supporting long-term cell stability.
Trade-offs
- Precise hot sealing conditions required: The film requires hot sealing at 180-190°C with 0.2 MPa pressure and 2 sec dwell time, which demands accurately controlled heat sealing equipment for consistent results.
Every advanced material, component, equipment, and instrument in our catalog is backed by rigorous testing. We maintain strict internal quality management frameworks and align with CE conformity metrics to deliver transparent, reproducible performance data via our public open-science repository.
To request raw batch performance data, submit formal vendor registration paperwork, or execute a fast-turnaround R&D manufacturing loop, contact us at inquiry@atomfair.com.
Item is dispatched under the Atomfair Shipping & Delivery Framework (Free worldwide shipping on orders over $59 USD excl. heavy equipment). Return is governed by the Atomfair Return & Refund Policy (7-day technical return window).