86 μm 200 mm×10 m Roll Aluminum-Plastic Film
POUCH CELL ALUMINUM-PLASTIC FILM
|
|||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
Purchase ConfirmationConfiguration: Confirm thickness, width, and length before ordering. Quotation Check: Confirm the title dimensions and pack format before production or ordering release.
|
Brand: ATOMFAIR®
Hot sealing must be conducted at 180–190°C for proper bond integrity. The laminate requires solvent retention below 5 mg/m² and exhibits a moisture vapor transmission rate of 200 ppm over 5 years.
- Hot Sealing Temperature: The film must be heat sealed within the temperature range of 180–190°C to achieve proper bond integrity.
- Heat Seal Strength: The heat seal strength must exceed 29.4 N/15 mm when tested at 200°C, 0.2 MPa, and 2 seconds.
- Laminate Strength: The laminate strength between nylon and aluminum must be greater than 2 N/15 mm, and between aluminum and CPP must be greater than 5 N/15 mm.
- Solvent Retention: Solvent retention must be less than 5 mg/m² to prevent contamination of the pouch cell.
- Molding Depth: The film supports a molding depth of at least 5.0 mm for pouch formation.
What minimum laminate strength and heat seal strength does the 86 μm aluminum-plastic film provide?
The laminate strength is specified as Nylon/Al more than 2 N/15 mm and Al/CPP more than 5 N/15 mm. Heat seal strength exceeds 29.4 N/15 mm at 200°C, 0.2 MPa, and 2 seconds on heatsealing equipment.
What hot sealing conditions are required for this pouch cell aluminum-plastic film?
The recommended hot sealing condition is 180–190°C. The heat seal strength test is performed at 200°C, 0.2 MPa, and 2 seconds, indicating the required sealing parameters for optimal bonding.
What are the solvent retention and moisture vapor transmission rate specifications for long-term storage of this film?
Solvent retention is less than 5 mg/m², and the moisture vapor/O2 transmission rate is 200 ppm over 5 years, ensuring low permeability and extended shelf life for pouch cell applications.
This 86 μm aluminum-plastic film, supplied as a 200 mm × 10 m roll, combines a 40 μm aluminum core with 25 μm polyamide and 40 μm polypropylene layers; the ≥5.0 mm molding depth and >29.4 N/15 mm heat seal strength support pouch forming and sealing, though the 180–190°C hot-sealing requirement and 200 ppm/5-year transmission rating define its processing and storage envelope.
Positive
- Multilayer laminate with ≥5.0 mm molding depth: The polyamide/aluminum/polypropylene construction provides a molding depth of at least 5.0 mm, supporting pouch forming and prototype assembly.
- High heat seal and laminate strength: Heat seal strength exceeds 29.4 N/15 mm at 200°C × 0.2 MPa × 2 s, with Al/CPP laminate strength above 5 N/15 mm, enabling robust pouch seals under controlled heat-sealing conditions.
Trade-offs
- Requires hot sealing at 180–190°C: Rated hot sealing conditions are 180–190°C, so users must have heat-sealing equipment capable of holding temperature, pressure, and dwell time to achieve the specified seal strength.
- Finite barrier performance over five years: Moisture vapor and O2 transmission is specified as 200 ppm / 5 years, meaning long-duration cell storage is bounded by the film's barrier rate and may require dry or controlled storage conditions.
Every advanced material, component, equipment, and instrument in our catalog is backed by rigorous testing. We maintain strict internal quality management frameworks and align with CE conformity metrics to deliver transparent, reproducible performance data via our public open-science repository.
To request raw batch performance data, submit formal vendor registration paperwork, or execute a fast-turnaround R&D manufacturing loop, contact us at inquiry@atomfair.com.
Item is dispatched under the Atomfair Shipping & Delivery Framework (Free worldwide shipping on orders over $59 USD excl. heavy equipment). Return is governed by the Atomfair Return & Refund Policy (7-day technical return window).